| Model | iPhone XR/11 3D HD | |
| Material | Glass | Xuhong high aluminosilicate glass |
| Japanese AB lamination | Use layers 270um | |
| A side release film 50um | ||
| B side release film 70um | ||
| Fingerprint oil | Japanese Daikin fingerprint oil | |
| With white PC back panel | Empty with ears (thickness 0.80MM) | |
| Craftsmanship | Thickness | Glass thickness 0.36mm Arc height：0.68mm Overall Thickness (without back plate) 0.63mm |
| Transmittance（Glass） | ≥92% | |
| Hardness | 9H | |
| Tempering time | 4 hours | |
| Inks | 1:1 (original phone color) | |
| Test items | Criteria | |
| Performance Testing | Trial patch test | The internal arc conformity is <0.15, and it is not easy for dust to enter |
| Very good exhaust performance, strong adsorption, no bubbles | ||
| No scratching on the edges | ||
| No gaps, the entire piece is made of glass | ||
| There is no white border on the screen | ||
| Touch sensitivity test | After the product is attached to the phone, there should be no problems affecting the touch control. | |
| Transmission test | Transmittance≧92% | |
| Toughness test | Can be bent 90° and U-shaped, not fragile edges | |
| Drop ball test | Drop ball test64G steel ball, 60CM impact the center point three times without breaking | |
| Water drop angle test | The water drop angle is 115°; after rubbing 5000 times with 1*1 0000# 1KG, the water drop angle is above 100° | |
| Surface Pencil Hardness Test | Use Mitsubishi Pencil 9H with a load of 500g and draw 3 lines on the surface without scratches. | |